23% AL2O3 Inert Alumina keramika Polo lagolago faʻapaʻepaʻe polo
E lautele faʻaaogaina i le suauʻu, vailaʻau, faʻapala, kesi ma siosiomaga puipuiga puipuiga, o se mafuaʻaga i le reactor e ufiufi lagolago mea ma olo teuina. E i ai le maualuga vevela ma maualuga uunaiga tetee, bibling fua faatatau maualalo, o le uiga o le vailaau faatinoga o fale o manu. E mafai ona tatalia le tafia o le acid, alkali ma isi meaola oona, ma mafai ona tumau i le gaosiga o gaioiga o le vevela suiga. O lona autu aoga o le faʻateleina kesi poʻo suavai tufatufaina itu, lagolago ma le puipuiga malosi e le maualuga gaioiga o le faʻatupuina.
Vailaʻau Fausiaina o le 23% AL2O3 Inert Alumina Polo keramika
|
Al2O3 + SiO2 |
Al2O3 |
Fe2O3 |
CaO |
MgO |
K2O + Na2O |
Isi |
|
> 93% |
23% |
<1% |
<0.5% |
<0.5% |
<4% |
<0.5% |
Leach mafai Fe2O3 e laʻititi ifo i le 0.1%.
Faʻaletino meatotino o le 23% AL2O3 Inert Alumina Polo keramika
|
Aitema |
Taua |
|
Mitiia le suavai (%) |
> 0.5 |
|
Tele tele (g / cm3) |
1.35-1.41 |
|
Malosiaga faʻapitoa (g / cm3) |
2.3-2.4 |
|
Tele fua (%) |
40% |
|
Faagaioiga temp. (Max) (℃) |
1250 |
|
Faigata a Moh (fua) |
> 6.5 |
|
Tetee oona (%) |
> 98 |
|
Tetee Alkali (%) |
>92 |
Tipi Malosi o le 23% AL2O3 Inert Alumina Pepa Keramika
|
Tele |
Tipi malosi |
|
|
Kg / fasimea |
KN / fasimea |
|
|
1/8 ″ (3mm) |
> 35 |
> 0.35 |
|
1/4 ″ (6mm) |
> 60 |
> 0.60 |
|
3/8 ″ (10mm) |
> 85 |
> 0.85 |
|
1/2 ″ (13mm) |
> 185 |
> 1.85 |
|
3/4 ″ (19mm) |
> 487 |
> 4.87 |
|
1 ″ (25mm) |
> 850 |
> 8.5 |
|
1-1 / 2 ″ (38mm) |
> 1200 |
> 12 |
|
2 ″ (50mm) |
> 5600 |
> 56 |
Tele ma le faapalepale o le 23% AL2O3 Inert Alumina Polo Keramika
|
Tele ma le faapalepale (mm) |
||||
|
Tele |
3/6/9 |
9/13 |
19/25/38 |
50 |
|
Faapalepale |
± 1.0 |
± 1.5 |
± 2 |
± 2.5 |